Materials ingredient list
JIS stainless steel ingredient table 1
Of the type
Sign
SUS
| Chemical ingredient (%)
| ||||||||
C
| Si
| Mn
| P
| S
| Ni
| Cr
| Mo
| Cu
| |
Austenite system
| |||||||||
201
| ≤0.15
| ≤1.00
| 5.50 ...
7.50
| ≤0.060
| ≤0.030
| 3.50 ...
5.50
| 16.00 ...
18.00
| －
| －
|
202
| ≤0.15
| ≤1.00
| 7.50 ...
10.00
| ≤0.060
| ≤0.030
| 4.00 ...
6.00
| 17.00 ...
19.00
| －
| －
|
301
| ≤0.15
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 6.00 ...
8.00
| 16.00 ...
18.00
| －
| －
|
301 L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 6.00 ...
8.00
| 16.00 ...
18.00
| －
| －
|
301J1
| 0.08 ...
0.12
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 7.00 ...
9.00
| 16.00 ...
18.00
| －
| －
|
302
| ≤0.15
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.00 ...
10.00
| 17.00 ...
19.00
| －
| －
|
302B
| ≤0.15
| 2.00 ...
3.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.00 ...
10.00
| 17.00 ...
19.00
| －
| －
|
303
| ≤0.15
| ≤1.00
| ≤2.00
| ≤2.00
| ≤0.15
| 8.00 ...
10.00
| 17.00 ...
19.00
| (1)
| －
|
303Cu
| ≤0.08
| ≤1.00
| ≤2.50
| ≤2.00
| ≤0.25
| 8.00 ...
10.00
| 17.00 ...
19.00
| (1)
| 2.50 ...
4.00
|
303Se
| ≤0.15
| ≤1.00
| ≤2.00
| ≤2.00
| ≤0.60
| 8.00 ...
10.00
| 17.00 ...
19.00
| －
| －
|
304
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.00 ...
10.50
| 18.00 ...
20.00
| －
| －
|
304 L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 9.00 ...
13.00
| 18.00 ...
20.00
| －
| －
|
304N1
| ≤0.08
| ≤1.00
| ≤2.50
| ≤0.045
| ≤0.030
| 7.00 ...
10.50
| 18.00 ...
20.00
| －
| －
|
304N2
| ≤0.08
| ≤1.00
| ≤2.50
| ≤0.045
| ≤0.030
| 7.50 ...
10.50
| 18.00 ...
20.00
| －
| －
|
304LN
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.50 ...
11.50
| 17.00 ...
19.00
| －
| －
|
304J1
| ≤0.08
| ≤1.70
| ≤3.00
| ≤0.045
| ≤0.030
| 6.00 ...
9.00
| 15.00 ...
18.00
| －
| 1.00 ...
3.00
|
304J2
| ≤0.08
| ≤1.70
| 3.00 ...
5.00
| ≤0.045
| ≤0.030
| 6.00 ...
9.00
| 15.00 ...
18.00
| －
| 1.00 ...
3.00
|
304J3
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.00 ...
10.50
| 17.00 ...
19.00
| －
| 1.00 ...
3.00
|
305
| ≤0.12
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.50 ...
13.00
| 17.00 ...
19.00
| －
| －
|
305J1
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.00 ...
13.50
| 16.50 ...
19.00
| －
| －
|
309S
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 12.00 ...
15.00
| 22.00 ...
24.00
| －
| －
|
310S
| ≤0.08
| ≤1.50
| ≤2.00
| ≤0.045
| ≤0.030
| 19.00 ...
22.00
| 24.00 ...
26.00
| －
| －
|
JIS stainless steel ingredient table 2
Of the type
Sign
SUS
| Chemical ingredient (%)
| ||||||||
C
| Si
| Mn
| P
| S
| Ni
| Cr
| Mo
| Cu
| |
Austenite system
| |||||||||
316
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.00 ...
14.00
| 16.00 ...
18.00
| 2.00 ...
3.00
| －
|
316 L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 12.00 ...
15.00
| 16.00 ...
18.00
| 2.00 ...
3.00
| －
|
316N
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.00 ...
14.00
| 16.00 ...
18.00
| 2.00 ...
3.00
| －
|
316LN
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.50 ...
14.50
| 16.50 ...
18.50
| 2.00 ...
3.00
| －
|
316Ti
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.00 ...
14.00
| 16.00 ...
18.00
| 2.00 ...
3.00
| －
|
316J1
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.00 ...
14.00
| 17.00 ...
19.00
| 1.20 ...
2.75
| 1.00 ...
2.50
|
316J1L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 12.00 ...
16.00
| 17.00 ...
19.00
| 1.20 ...
2.75
| 1.00 ...
2.50
|
316F
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.10
| 10.00 ...
14.00
| 16.00 ...
18.00
| 2.00 ...
3.00
| －
|
317
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.00 ...
15.00
| 18.00 ...
20.00
| 3.00 ...
4.00
| －
|
317 L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.00 ...
15.00
| 18.00 ...
20.00
| 3.00 ...
4.00
| －
|
317LN
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.00 ...
15.00
| 18.00 ...
20.00
| 3.00 ...
4.00
| －
|
317J1
| ≤0.040
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 15.00 ...
17.00
| 16.00 ...
19.00
| 4.00 ...
6.00
| －
|
317J2
| ≤0.06
| ≤1.50
| ≤2.00
| ≤0.045
| ≤0.030
| 12.00 ...
16.00
| 23.00 ...
26.00
| 0.50 ...
1.20
| －
|
317J3L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.00 ...
13.00
| 20.50 ...
22.50
| 2.00 ...
3.00
| －
|
317J4L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 24.00 ...
26.00
| 19.00 ...
24.00
| 5.00 ...
7.00
| －
|
317J5L
| ≤0.020
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 23.00 ...
28.00
| 19.00 ...
23.00
| 4.00 ...
5.00
| 1.00 ...
2.00
|
321
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 9.00 ...
13.00
| 17.00 ...
19.00
| －
| －
|
347
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 9.00 ...
13.00
| 17.00 ...
19.00
| －
| －
|
384
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 17.00 ...
19.00
| 15.00 ...
17.00
| －
| －
|
XM7
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.50 ...
10.50
| 17.00 ...
19.00
| －
| 3.00 ...
4.00
|
XM15J1
| ≤0.08
| 3.00 ...
5.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.50 ...
15.00
| 15.00 ...
20.00
| －
| －
|
Austenite ferrite system
| |||||||||
329J1
| ≤0.08
| ≤1.00
| ≤1.50
| ≤0.040
| ≤0.030
| 3.00 ...
6.00
| 23.00 ...
28.00
| 1.00 ...
3.00
| －
|
329J3L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.040
| ≤0.030
| 4.50 ...
6.50
| 21.00 ...
24.00
| 2.50-3.50
| －
|
329J4L
| ≤0.030
| ≤1.00
| ≤1.50
| ≤0.040
| ≤0.030
| 5.50 ...
7.50
| 24.00 ...
26.00
| 2.50 ...
3.50
| －
|
JIS stainless steel ingredient table 3
Of the type
Sign
SUS
| Chemical ingredient (%)
| ||||||||
C
| Si
| Mn
| P
| S
| Ni
| Cr
| Mo
| Cu
| |
Ferrite system
| |||||||||
405
| ≤0.08
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50 ...
14.50
| －
| －
|
410 L
| ≤0.030
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.00 ...
13.50
| －
| －
|
429
| ≤0.12
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 14.00 ...
16.00
| －
| －
|
430
| ≤0.12
| ≤0.75
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00 ...
18.00
| －
| －
|
430F
| ≤0.12
| ≤1.00
| ≤1.25
| ≤0.060
| ≤0.015
| (2)
| 16.00 ...
18.00
| (1)
| －
|
430LX
| ≤0.030
| ≤0.75
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00 ...
19.00
| －
| －
|
430J1L
| ≤0.025
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00 ...
20.00
| －
| 0.30 ...
0.80
|
434
| ≤0.12
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.10
| (2)
| 16.00 ...
18.00
| 0.75 ...
1.25
| －
|
436 L
| ≤0.025
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00 ...
19.00
| 0.75 ...
1.25
| －
|
436J1L
| ≤0.025
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 17.00 ...
20.00
| 0.40 ...
0.80
| －
|
444
| ≤0.025
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 17.00 ...
20.00
| 1.75 ...
2.50
| －
|
447J1
| ≤0.010
| ≤0.40
| ≤0.40
| ≤0.030
| ≤0.020
| (4)
| 28.50 ...
32.00
| 1.50 ...
2.50
| (4)
|
XM27
| ≤0.010
| ≤0.40
| ≤0.40
| ≤0.030
| ≤0.020
| (4)
| 25.00 ...
27.50
| 0.75 ...
1.50
| (4)
|
Martensite system
| |||||||||
403
| ≤0.15
| ≤0.50
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50 ...
13.00
| －
| －
|
410
| ≤0.15
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50 ...
13.50
| －
| －
|
410S
| ≤0.08
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50 ...
13.50
| －
| －
|
410F2
| ≤0.15
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50 ...
13.50
| －
| －
|
410J1
| 0.08 ...
0.18
| ≤0.60
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50 ...
14.00
| 0.30 ...
0.60
| －
|
416
| ≤0.15
| ≤1.00
| ≤1.25
| ≤0.060
| ≤0.015
| (2)
| 12.00 ...
14.00
| (1)
| －
|
420J1
| 0.16 ...
0.25
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 12.00 ...
14.00
| －
| －
|
420J2
| 0.26 ...
0.40
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 12.00 ...
14.00
| －
| －
|
420F
| 0.26 ...
0.40
| ≤1.00
| ≤1.25
| ≤0.060
| ≤0.015
| (2)
| 12.00 ...
14.00
| (1)
| －
|
420F2
| 0.26 ...
0.40
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 12.00 ...
14.00
| －
| －
|
429J1
| 0.25 ...
0.40
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 15.00 ...
17.00
| －
| －
|
431
| ≤0.20
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| 1.25 ...
2.50
| 15.00 ...
17.00
| －
| －
|
440A
| 0.60 ...
0.75
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00 ...
18.00
| (3)
| －
|
440B
| 0.75 ...
0.95
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00 ...
18.00
| (3)
| －
|
440C
| 0.95 ...
1.20
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00 ...
18.00
| (3)
| －
|
440F
| 0.95 ...
1.20
| ≤1.00
| ≤1.25
| ≤0.060
| ≤0.015
| (2)
| 16.00 ...
18.00
| (3)
| －
|
Separation hardening system
| |||||||||
630
| ≤0.07
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| 3.00 ...
5.00
| 15.00 ...
17.50
| －
| 3.00 ...
5.00
|
631
| ≤0.09
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| 6.50 ...
7.75
| 16.00 ...
18.00
| －
| －
|
631J1
| ≤0.09
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| 7.00 ...
8.50
| 16.00 ...
18.00
| －
| －
|
※Note
- The Mo can add 0.60% or less.
- Ni may contain 0.60% or less.
- The Mo can add 0.75% or less.
- You may contain Nio 0.50% or less, Cu 0.20% or less and Ni+Cu 0.50% or less.
Remarks: SUS329J1, SUS329J3L, SUS329J4L, SUS447J1, SUSXM27 and SUSXM15J1 can add the alloy element except the table.
Galvanizing iron wire S (JIS G 3547)
Type | Sign | Coverage | Official name diameter (mm) Representative namono | Line diameter
Allowance
(mm) | Tensile strength
(N/ heihometoru) | Growth
(%) | Torsion
(time) | Zinc
Quantity of adhesion
(g/ heihometoru) | With winding
Of the line diameter
Multiple |
Galvanizing iron wire S | SWMGS-2
Two kinds | 0.1-8.0 | 1.60 | ±0.05 | － | － | － | 20 or more | － |
2.00 | 290-540 | 25 or more | |||||||
2.60 | ±0.07 | ||||||||
3.20 | 30 or more | ||||||||
4.00 | ±0.08 | 35 or more | |||||||
5.00 | ±0.10 | 45 or more | |||||||
6.00 | ±0.12 | 50 or more | |||||||
SWMGS-3
Three kinds | 2.0-10.0 | 2.60 | ±0.07 | 290-540 | 10 or more | 39 | 120 or more | 3 | |
3.20 | 30 | 135 or more | |||||||
4.00 | ±0.08 | 24 | 155 or more | 4 | |||||
5.00 | ±0.10 | 20 | |||||||
6.00 | ±0.12 | 15 | |||||||
SWMGS-4
Four kinds | 1.6-10.0 | 2.60 | ±0.07 | 290-540 | 10 or more | 33 | 185 or more | 4 | |
3.20 | 26 | 230 or more | |||||||
4.00 | ±0.08 | 21 | 245 or more | 5 | |||||
5.00 | ±0.10 | 17 | |||||||
6.00 | ±0.12 | 13 | |||||||
SWMGS-5
Five kinds | 1.6-10.0 | 2.60 | ±0.07 | 290-540 | 10 or more | 33 | 230 or more | 4 | |
3.20 | 26 | 270 or more | |||||||
4.00 | ±0.08 | 21 | 290 or more | 5 | |||||
5.00 | ±0.10 | 17 | |||||||
6.00 | ±0.12 | 13 | |||||||
SWMGS-6
Six kinds | 1.6-10.0 | 2.60 | ±0.09 | 290-540 | 10 or more | 33 | 300 or more | 4 | |
3.20 | 26 | ||||||||
4.00 | ±0.10 | 21 | 5 | ||||||
5.00 | ±0.12 | 17 | |||||||
6.00 | 13 | ||||||||
SWMGS-7
Seven kinds | 1.6-10.0 | 2.60 | ±0.09 | 290-540 | 10 or more | 33 | 400 or more | 4 | |
3.20 | 26 | ||||||||
4.00 | ±0.10 | 21 | 5 | ||||||
5.00 | ±0.12 | 17 | |||||||
6.00 | 13 |
Galvanizing iron wire H (JIS G 3547)
Type | Sign | Coverage | Official name diameter (mm) Representative namono | Line diameter
Allowance
(mm) | Tensile strength
(N/ heihometoru) | Growth
(%) | Torsion
(time) | Zinc
Quantity of adhesion
(g/ heihometoru) | With winding
Of the line diameter
Multiple |
Galvanizing iron wire H | SWMGH-2
Two kinds | 2.0-8.0 | 2.60 | ±0.06 | 590-880 | － | － | 25 or more | － |
3.20 | 540-830 | 30 or more | |||||||
4.00 | ±0.07 | 390-780 | 35 or more | ||||||
5.00 | ±0.08 | 45 or more | |||||||
6.00 | 50 or more | ||||||||
SWMGH-3
Three kinds | 2.0-10.0 | 2.60 | ±0.06 | 590-880 | － | － | 120 or more | 3 | |
3.20 | 540-830 | 135 or more | |||||||
4.00 | ±0.07 | 390-780 | 155 or more | 4 | |||||
5.00 | ±0.08 | ||||||||
6.00 | |||||||||
SWMGH-4
Four kinds | 1.6-10.0 | 2.60 | ±0.06 | 590-880 | － | － | 185 or more | 4 | |
3.20 | 540-830 | 230 or more | |||||||
4.00 | ±0.07 | 390-780 | 245 or more | 5 | |||||
5.00 | ±0.08 | ||||||||
6.00 |
Titanium alloy
Standard | Chemical ingredient (%) | ||||||
JS | ASTM | H | O | N | C | Fe | Ti |
TW28 | Grade1 | 0.0125 or less | 0.15 or less | 0.03 or less | 0.10 or less | 0.20 or less | Residue |
TW35 | Grade2 | 0.0125 or less | 0.20 or less | 0.03 or less | 0.10 or less | 0.25 or less | Residue |
TW49 | Grade3 | 0.0125 or less | 0.30 or less | 0.05 or less | 0.10 or less | 0.30 or less | Residue |
Copper wire for the heat-resistant Wire Cloth
Classification | Chemical ingredient (%) | ||||||||
JS, ASI | C | Si | Mn | P | S | Ni | Cr | Mo | Others |
SUS309 | ≤0.20 | ≤1.00 | ≤2.00 | ≤0.040 | ≤0.030 | 12.00
...
15.00 | 22.00
...
24.00 | － | － |
SUS309S | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.030 | 12.00
...
15.00 | 22.00
...
24.00 | － | － |
SUS310 | ≤0.25 | ≤1.50 | ≤2.00 | ≤0.040 | ≤0.030 | 19.00
...
22.00 | 24.00
...
26.00 | － | － |
SUS310S | ≤0.08 | ≤1.50 | ≤2.00 | ≤0.045 | ≤0.030 | 19.00
...
22.00 | 24.00
...
26.00 | － | － |
SUS314 | ≤0.25 | 1.50
...
3.00 | ≤2.00 | ≤0.040 | ≤0.030 | 19.00
...
22.00 | 23.00
...
26.00 | － | － |
SUH330 | ≤0.15 | ≤1.50 | ≤2.00 | ≤0.040 | ≤0.030 | 33.00
...
37.00 | 14.00
...
17.00 | － | － |
NCF800 | ≤0.10 | ≤1.00 | ≤1.50 | ≤0.030 | ≤0.015 | 30.00
...
35.00 | 19.00
...
23.00 | ≤0.60 | |
NCF600 | ≤0.15 | ≤0.50 | ≤1.00 | ≤0.030 | ≤0.015 | Ni+Co
72.00
The above | 14.00
...
17.00 | ≤0.60 | Cu0.50
The following
Fe6.00
...
10.00 |
NCF601 | ≤0.10 | ≤0.50 | ≤1.00 | ≤0.030 | ≤0.015 | 58.00
...
63.00 | 21.00
...
25.00 | － | |
NOH
nikuro
metto | ≤0.15 | 0.75
...
1.50 | ≤2.50 | － | － | 77.00
The above | 19.00
...
21.00 | － | － |