材料成分表
JIS ステンレス鋼成分表 1
種類の
記号
SUS
| 化学成分(%)
| ||||||||
C
| Si
| Mn
| P
| S
| Ni
| Cr
| Mo
| Cu
| |
オーステナイト系
| |||||||||
201
| ≤0.15
| ≤1.00
| 5.50~
7.50
| ≤0.060
| ≤0.030
| 3.50~
5.50
| 16.00~
18.00
| -
| -
|
202
| ≤0.15
| ≤1.00
| 7.50~
10.00
| ≤0.060
| ≤0.030
| 4.00~
6.00
| 17.00~
19.00
| -
| -
|
301
| ≤0.15
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 6.00~
8.00
| 16.00~
18.00
| -
| -
|
301L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 6.00~
8.00
| 16.00~
18.00
| -
| -
|
301J1
| 0.08~
0.12
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 7.00~
9.00
| 16.00~
18.00
| -
| -
|
302
| ≤0.15
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.00~
10.00
| 17.00~
19.00
| -
| -
|
302B
| ≤0.15
| 2.00~
3.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.00~
10.00
| 17.00~
19.00
| -
| -
|
303
| ≤0.15
| ≤1.00
| ≤2.00
| ≤2.00
| ≤0.15
| 8.00~
10.00
| 17.00~
19.00
| (1)
| -
|
303Cu
| ≤0.08
| ≤1.00
| ≤2.50
| ≤2.00
| ≤0.25
| 8.00~
10.00
| 17.00~
19.00
| (1)
| 2.50~
4.00
|
303Se
| ≤0.15
| ≤1.00
| ≤2.00
| ≤2.00
| ≤0.60
| 8.00~
10.00
| 17.00~
19.00
| -
| -
|
304
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.00~
10.50
| 18.00~
20.00
| -
| -
|
304L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 9.00~
13.00
| 18.00~
20.00
| -
| -
|
304N1
| ≤0.08
| ≤1.00
| ≤2.50
| ≤0.045
| ≤0.030
| 7.00~
10.50
| 18.00~
20.00
| -
| -
|
304N2
| ≤0.08
| ≤1.00
| ≤2.50
| ≤0.045
| ≤0.030
| 7.50~
10.50
| 18.00~
20.00
| -
| -
|
304LN
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.50~
11.50
| 17.00~
19.00
| -
| -
|
304J1
| ≤0.08
| ≤1.70
| ≤3.00
| ≤0.045
| ≤0.030
| 6.00~
9.00
| 15.00~
18.00
| -
| 1.00~
3.00
|
304J2
| ≤0.08
| ≤1.70
| 3.00~
5.00
| ≤0.045
| ≤0.030
| 6.00~
9.00
| 15.00~
18.00
| -
| 1.00~
3.00
|
304J3
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.00~
10.50
| 17.00~
19.00
| -
| 1.00~
3.00
|
305
| ≤0.12
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.50~
13.00
| 17.00~
19.00
| -
| -
|
305J1
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.00~
13.50
| 16.50~
19.00
| -
| -
|
309S
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 12.00~
15.00
| 22.00~
24.00
| -
| -
|
310S
| ≤0.08
| ≤1.50
| ≤2.00
| ≤0.045
| ≤0.030
| 19.00~
22.00
| 24.00~
26.00
| -
| -
|
JIS ステンレス鋼成分表 2
種類の
記号
SUS
| 化学成分(%)
| ||||||||
C
| Si
| Mn
| P
| S
| Ni
| Cr
| Mo
| Cu
| |
オーステナイト系
| |||||||||
316
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.00~
14.00
| 16.00~
18.00
| 2.00~
3.00
| -
|
316L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 12.00~
15.00
| 16.00~
18.00
| 2.00~
3.00
| -
|
316N
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.00~
14.00
| 16.00~
18.00
| 2.00~
3.00
| -
|
316LN
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.50~
14.50
| 16.50~
18.50
| 2.00~
3.00
| -
|
316Ti
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.00~
14.00
| 16.00~
18.00
| 2.00~
3.00
| -
|
316J1
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 10.00~
14.00
| 17.00~
19.00
| 1.20~
2.75
| 1.00~
2.50
|
316J1L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 12.00~
16.00
| 17.00~
19.00
| 1.20~
2.75
| 1.00~
2.50
|
316F
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.10
| 10.00~
14.00
| 16.00~
18.00
| 2.00~
3.00
| -
|
317
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.00~
15.00
| 18.00~
20.00
| 3.00~
4.00
| -
|
317L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.00~
15.00
| 18.00~
20.00
| 3.00~
4.00
| -
|
317LN
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.00~
15.00
| 18.00~
20.00
| 3.00~
4.00
| -
|
317J1
| ≤0.040
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 15.00~
17.00
| 16.00~
19.00
| 4.00~
6.00
| -
|
317J2
| ≤0.06
| ≤1.50
| ≤2.00
| ≤0.045
| ≤0.030
| 12.00~
16.00
| 23.00~
26.00
| 0.50~
1.20
| -
|
317J3L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.00~
13.00
| 20.50~
22.50
| 2.00~
3.00
| -
|
317J4L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 24.00~
26.00
| 19.00~
24.00
| 5.00~
7.00
| -
|
317J5L
| ≤0.020
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 23.00~
28.00
| 19.00~
23.00
| 4.00~
5.00
| 1.00~
2.00
|
321
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 9.00~
13.00
| 17.00~
19.00
| -
| -
|
347
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 9.00~
13.00
| 17.00~
19.00
| -
| -
|
384
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 17.00~
19.00
| 15.00~
17.00
| -
| -
|
XM7
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 8.50~
10.50
| 17.00~
19.00
| -
| 3.00~
4.00
|
XM15J1
| ≤0.08
| 3.00~
5.00
| ≤2.00
| ≤0.045
| ≤0.030
| 11.50~
15.00
| 15.00~
20.00
| -
| -
|
オーステナイト・フェライト系
| |||||||||
329J1
| ≤0.08
| ≤1.00
| ≤1.50
| ≤0.040
| ≤0.030
| 3.00~
6.00
| 23.00~
28.00
| 1.00~
3.00
| -
|
329J3L
| ≤0.030
| ≤1.00
| ≤2.00
| ≤0.040
| ≤0.030
| 4.50~
6.50
| 21.00~
24.00
| 2.50~3.50
| -
|
329J4L
| ≤0.030
| ≤1.00
| ≤1.50
| ≤0.040
| ≤0.030
| 5.50~
7.50
| 24.00~
26.00
| 2.50~
3.50
| -
|
JIS ステンレス鋼成分表 3
種類の
記号
SUS
| 化学成分(%)
| ||||||||
C
| Si
| Mn
| P
| S
| Ni
| Cr
| Mo
| Cu
| |
フェライト系
| |||||||||
405
| ≤0.08
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50~
14.50
| -
| -
|
410L
| ≤0.030
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.00~
13.50
| -
| -
|
429
| ≤0.12
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 14.00~
16.00
| -
| -
|
430
| ≤0.12
| ≤0.75
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00~
18.00
| -
| -
|
430F
| ≤0.12
| ≤1.00
| ≤1.25
| ≤0.060
| ≤0.015
| (2)
| 16.00~
18.00
| (1)
| -
|
430LX
| ≤0.030
| ≤0.75
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00~
19.00
| -
| -
|
430J1L
| ≤0.025
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00~
20.00
| -
| 0.30~
0.80
|
434
| ≤0.12
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.10
| (2)
| 16.00~
18.00
| 0.75~
1.25
| -
|
436L
| ≤0.025
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00~
19.00
| 0.75~
1.25
| -
|
436J1L
| ≤0.025
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 17.00~
20.00
| 0.40~
0.80
| -
|
444
| ≤0.025
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 17.00~
20.00
| 1.75~
2.50
| -
|
447J1
| ≤0.010
| ≤0.40
| ≤0.40
| ≤0.030
| ≤0.020
| (4)
| 28.50~
32.00
| 1.50~
2.50
| (4)
|
XM27
| ≤0.010
| ≤0.40
| ≤0.40
| ≤0.030
| ≤0.020
| (4)
| 25.00~
27.50
| 0.75~
1.50
| (4)
|
マルテンサイト系
| |||||||||
403
| ≤0.15
| ≤0.50
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50~
13.00
| -
| -
|
410
| ≤0.15
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50~
13.50
| -
| -
|
410S
| ≤0.08
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50~
13.50
| -
| -
|
410F2
| ≤0.15
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50~
13.50
| -
| -
|
410J1
| 0.08~
0.18
| ≤0.60
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 11.50~
14.00
| 0.30~
0.60
| -
|
416
| ≤0.15
| ≤1.00
| ≤1.25
| ≤0.060
| ≤0.015
| (2)
| 12.00~
14.00
| (1)
| -
|
420J1
| 0.16~
0.25
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 12.00~
14.00
| -
| -
|
420J2
| 0.26~
0.40
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 12.00~
14.00
| -
| -
|
420F
| 0.26~
0.40
| ≤1.00
| ≤1.25
| ≤0.060
| ≤0.015
| (2)
| 12.00~
14.00
| (1)
| -
|
420F2
| 0.26~
0.40
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 12.00~
14.00
| -
| -
|
429J1
| 0.25~
0.40
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 15.00~
17.00
| -
| -
|
431
| ≤0.20
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| 1.25~
2.50
| 15.00~
17.00
| -
| -
|
440A
| 0.60~
0.75
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00~
18.00
| (3)
| -
|
440B
| 0.75~
0.95
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00~
18.00
| (3)
| -
|
440C
| 0.95~
1.20
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| (2)
| 16.00~
18.00
| (3)
| -
|
440F
| 0.95~
1.20
| ≤1.00
| ≤1.25
| ≤0.060
| ≤0.015
| (2)
| 16.00~
18.00
| (3)
| -
|
析出硬化系
| |||||||||
630
| ≤0.07
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| 3.00~
5.00
| 15.00~
17.50
| -
| 3.00~
5.00
|
631
| ≤0.09
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| 6.50~
7.75
| 16.00~
18.00
| -
| -
|
631J1
| ≤0.09
| ≤1.00
| ≤1.00
| ≤0.040
| ≤0.030
| 7.00~
8.50
| 16.00~
18.00
| -
| -
|
※注
- Moは、0.60%以下を添加することができる。
- Niは、0.60%以下を含有してもよい。
- Moは、0.75%以下を添加することができる。
- Nio 0.50%以下、Cu 0.20%以下、及びNi+Cu 0.50%以下を含有してもよい。
備考:SUS329J1、SUS329J3L、 SUS329J4L、SUS447J1、SUSXM27及びSUSXM15J1は表以外の合金元素を添加することができる。
亜鉛めっき鉄線 S (JIS G 3547)
種類
| 記号
| 適用範囲
| 公称径
(mm) 代表的 なもの | 線径
許容差
(mm)
| 引張強さ
(N/㎡)
| 伸び
(%)
| ねじり
(回)
| 亜鉛
付着量
(g/㎡)
| 巻付
線径の
倍数
|
亜鉛めっき鉄線S
| SWMGS-2
2種
| 0.1~8.0
| 1.60
| ±0.05
| -
| -
| -
| 20以上
| -
|
2.00
| 290~540
| 25以上
| |||||||
2.60
| ±0.07
| ||||||||
3.20
| 30以上
| ||||||||
4.00
| ±0.08
| 35以上
| |||||||
5.00
| ±0.10
| 45以上
| |||||||
6.00
| ±0.12
| 50以上
| |||||||
SWMGS-3
3種
| 2.0~10.0
| 2.60
| ±0.07
| 290~540
| 10以上
| 39
| 120以上
| 3
| |
3.20
| 30
| 135以上
| |||||||
4.00
| ±0.08
| 24
| 155以上
| 4
| |||||
5.00
| ±0.10
| 20
| |||||||
6.00
| ±0.12
| 15
| |||||||
SWMGS-4
4種
| 1.6~10.0
| 2.60
| ±0.07
| 290~540
| 10以上
| 33
| 185以上
| 4
| |
3.20
| 26
| 230以上
| |||||||
4.00
| ±0.08
| 21
| 245以上
| 5
| |||||
5.00
| ±0.10
| 17
| |||||||
6.00
| ±0.12
| 13
| |||||||
SWMGS-5
5種
| 1.6~10.0
| 2.60
| ±0.07
| 290~540
| 10以上
| 33
| 230以上
| 4
| |
3.20
| 26
| 270以上
| |||||||
4.00
| ±0.08
| 21
| 290以上
| 5
| |||||
5.00
| ±0.10
| 17
| |||||||
6.00
| ±0.12
| 13
| |||||||
SWMGS-6
6種
| 1.6~10.0
| 2.60
| ±0.09
| 290~540
| 10以上
| 33
| 300以上
| 4
| |
3.20
| 26
| ||||||||
4.00
| ±0.10
| 21
| 5
| ||||||
5.00
| ±0.12
| 17
| |||||||
6.00
| 13
| ||||||||
SWMGS-7
7種
| 1.6~10.0
| 2.60
| ±0.09
| 290~540
| 10以上
| 33
| 400以上
| 4
| |
3.20
| 26
| ||||||||
4.00
| ±0.10
| 21
| 5
| ||||||
5.00
| ±0.12
| 17
| |||||||
6.00
| 13
|
亜鉛めっき鉄線 H (JIS G 3547)
種類
| 記号
| 適用範囲
| 公称径
(mm) 代表的 なもの | 線径
許容差
(mm)
| 引張強さ
(N/㎡)
| 伸び
(%)
| ねじり
(回)
| 亜鉛
付着量
(g/㎡)
| 巻付
線径の
倍数
|
亜鉛めっき鉄線H
| SWMGH-2
2種
| 2.0~8.0
| 2.60
| ±0.06
| 590~880
| -
| -
| 25以上
| -
|
3.20
| 540~830
| 30以上
| |||||||
4.00
| ±0.07
| 390~780
| 35以上
| ||||||
5.00
| ±0.08
| 45以上
| |||||||
6.00
| 50以上
| ||||||||
SWMGH-3
3種
| 2.0~10.0
| 2.60
| ±0.06
| 590~880
| -
| -
| 120以上
| 3
| |
3.20
| 540~830
| 135以上
| |||||||
4.00
| ±0.07
| 390~780
| 155以上
| 4
| |||||
5.00
| ±0.08
| ||||||||
6.00
| |||||||||
SWMGH-4
4種
| 1.6~10.0
| 2.60
| ±0.06
| 590~880
| -
| -
| 185以上
| 4
| |
3.20
| 540~830
| 230以上
| |||||||
4.00
| ±0.07
| 390~780
| 245以上
| 5
| |||||
5.00
| ±0.08
| ||||||||
6.00
|
チタン合金
規格
| 化学成分(%)
| ||||||
JS
| ASTM
| H
| O
| N
| C
| Fe
| Ti
|
TW28
| Grade1
| 0.0125以下
| 0.15以下
| 0.03以下
| 0.10以下
| 0.20以下
| 残部
|
TW35
| Grade2
| 0.0125以下
| 0.20以下
| 0.03以下
| 0.10以下
| 0.25以下
| 残部
|
TW49
| Grade3
| 0.0125以下
| 0.30以下
| 0.05以下
| 0.10以下
| 0.30以下
| 残部
|
耐熱金網用銅線
種別
| 化学成分(%)
| ||||||||
JS・ASI
| C
| Si
| Mn
| P
| S
| Ni
| Cr
| Mo
| その他
|
SUS309
| ≤0.20
| ≤1.00
| ≤2.00
| ≤0.040
| ≤0.030
| 12.00
~
15.00
| 22.00
~
24.00
| -
| -
|
SUS309S
| ≤0.08
| ≤1.00
| ≤2.00
| ≤0.045
| ≤0.030
| 12.00
~
15.00
| 22.00
~
24.00
| -
| -
|
SUS310
| ≤0.25
| ≤1.50
| ≤2.00
| ≤0.040
| ≤0.030
| 19.00
~
22.00
| 24.00
~
26.00
| -
| -
|
SUS310S
| ≤0.08
| ≤1.50
| ≤2.00
| ≤0.045
| ≤0.030
| 19.00
~
22.00
| 24.00
~
26.00
| -
| -
|
SUS314
| ≤0.25
| 1.50
~
3.00
| ≤2.00
| ≤0.040
| ≤0.030
| 19.00
~
22.00
| 23.00
~
26.00
| -
| -
|
SUH330
| ≤0.15
| ≤1.50
| ≤2.00
| ≤0.040
| ≤0.030
| 33.00
~
37.00
| 14.00
~
17.00
| -
| -
|
NCF800
| ≤0.10
| ≤1.00
| ≤1.50
| ≤0.030
| ≤0.015
| 30.00
~
35.00
| 19.00
~
23.00
| ≤0.60
| |
NCF600
| ≤0.15
| ≤0.50
| ≤1.00
| ≤0.030
| ≤0.015
| Ni+Co
72.00
以上
| 14.00
~
17.00
| ≤0.60
| Cu0.50
以下
Fe6.00
~
10.00
|
NCF601
| ≤0.10
| ≤0.50
| ≤1.00
| ≤0.030
| ≤0.015
| 58.00
~
63.00
| 21.00
~
25.00
| -
| |
NOH
ニクロ
メット
| ≤0.15
| 0.75
~
1.50
| ≤2.50
| -
| -
| 77.00
以上
| 19.00
~
21.00
| -
| -
|